S-Plastic Ultem PEI PW1000 Specific Grade-Colors Aredesigned And Certified For Use In Potable Water Applications

Name: SPlastic Ultem PEI PW1000 Specific GradeColors Aredesigned And Certified For Use In Potable Water Applications
Brand: S-Plastic
Price: 1 USD

Wholesale S-Plastic Ultem PEI PW1000 Specific Grade-Colors Aredesigned And Certified For Use In Potable Water Applications from china suppliers

Brand Name : S-Plastic

Model Number : PW1000

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD to be negotiated

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 360°C/5.0 kg : 13

Density : 1.27

Contact Now

Ultem PEI PW1000 is an Unfilled Standard flow Polyetherimide (Tg 217?C). Specific grade-colors aredesigned and certified for use in Potable Water applications. KTW, WRAS, ACS, NSF-61 and W270 certified. US FDA and European Food Contact approved.

Property

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Taber Abrasion, CS-17, 1 kg	10	mg/1000cy	S-Plastics method
Tensile Stress, yield, 50 mm/min	105	MPa	ISO 527
Tensile Stress, break, 50 mm/min	85	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	60	%	ISO 527
Tensile Modulus, 1 mm/min	3200	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	160	MPa	ISO 178
Flexural Modulus, 2 mm/min	3300	MPa	ISO 178
Hardness, H358/30	140	MPa	ISO 2039-1
IMPACT
Izod Impact, unnotched 80104 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80104 -30°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	6	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	4	kJ/m²	ISO 179/1eA
Charpy Impact, notched, 23°C	10	kJ/m²	ISO 179/2C
Charpy -30°C, V-notch Edgew 80104 sp=62mm	4	kJ/m²	ISO 179/1eA
THERMAL
Thermal Conductivity	0.24	W/m-°C	ISO 8302
CTE, 23°C to 150°C, flow	5.E-05	1/°C	ISO 11359-2
CTE, 23°C to 150°C, xflow	5.E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	215	°C	ISO 306
Vicat Softening Temp, Rate B/50	211	°C	ISO 306
Vicat Softening Temp, Rate B/120	215	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	200	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	190	°C	ISO 75/Ae

Processing

INJECTION MOLDING
Drying Temperature	150	°C
Drying Time	4 – 6	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	370 – 410	°C
Nozzle Temperature	350 – 405	°C
Front - Zone 3 Temperature	360 – 415	°C
Middle - Zone 2 Temperature	350 – 405	°C
Rear - Zone 1 Temperature	340 – 395	°C
Hopper Temperature	80 – 120	°C
Mold Temperature	140 – 180	°C

For more information please download the datasheet
	S S-Plastics Ultem PEI PW1000.pdf

Get The Latest Quotation

First-level distribution source in South China
Reduce procurement costs, improve supply stability,
Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

Product Tags: